淄博工泰商贸有限公司

牌号

Brand

型号

Modrel

线径

Wire

Diameter

熔敷金属化学成分(%)

Chemical Composition of Deposited Metal

用途

Applications

GB

JIS

AWS

C

Si

Mn

P

S

Cr

Ni

Mo

Cu

Other

ER308

H08Cr21Ni10

Y308

ER308

2.0-4.5

0.08

0.3-0.65

1.0-2.5

0.03

0.03

19.5-22.0

9.0-11.0

0.75

0.75

用于焊接18%Cr、8%Ni钢，具有良好的抗热裂性。

Be used to weld 18%Cr, 8%Ni steels, better heat-resistance crack-resistance。

ER308L

H03Cr21Ni10

Y308L

ER308L

2.0-4.5

0.03

0.3-0.65

1.0-2.5

0.03

0.03

19.5-22.0

9.0-11.0

0.75

0.75

用于焊接低碳18%Cr、8%Ni钢，耐裂性与耐蚀性均甚优良。

Be used to weld low-carbon 18%Cr, 8%Ni steels，better crack-resistance corrosion-resistance.

ER308LSi

H03Cr21Ni10Si1

Y308LSi

ER308LSi

2.0-4.5

0.03

0.65-1.0

1.0-2.5

0.03

0.03

19.5-22.0

9.0-11.0

0.75

0.75

熔敷金属流动性较308Ｌ为佳，在焊接操作上也更优越。

Deposited metal fluidity better than 308L, on weld the operation too more superior.

ER309

H12Cr24Ni13

Y309

ER309

2.0-4.5

0.12

0.3-0.65

1.0-2.5

0.03

0.03

23.0-25.0

12.0-14.0

0.75

0.75

用于22%Cr、12%Ni钢，以及软钢与不锈钢，铬钼钢等异种金属的焊接，耐热性与耐蚀性甚为优越。

Be used to weld 22%Cr, 12%Ni steels,and soft steel and stainless steel, chromium molybdenum steel, different race welding of metals, heat-resistance, corrosion-resistance bear the eclipse even superior.

ER309L

H03Cr24Ni13

Y309L

ER309L

2.0-4.5

0.03

0.3-0.65

1.0-2.5

0.03

0.03

23.0-25.0

12.0-14.0

0.75

0.75

用于低碳22%Cr、12%Ni钢，以及软钢与不锈钢，铬钼钢等异种金属的焊接，耐热性与耐蚀性甚为优越。

Be used to weld low-carbon 22%Cr, 12%Ni steels,and soft steel and stainless steel,chromium molybdenum steel, different race welding of metals, heat-resistance, corrosion-resistance bear the eclipse even superior.

ER310

H12Cr26Ni21

Y310

ER310

2.0-4.5

0.08-0.15

0.3-0.65

1.0-2.5

0.03

0.03

25.0-28.0

20.0-22.5

0.75

0.75

用于25%Cr、20%Ni钢，硬化性高的钢材以及异种金属的焊接。

Be used to weld 25%Cr, 20%Ni steels, hardening welding of high steel material and different race metals.

ER312

H15Cr30Ni9

Y312

ER312

2.0-4.5

0.15

0.3-0.65

1.0-2.5

0.03

0.03

28.0-32.0

8.0-10.5

0.75

0.75

用于29%Cr、9%Ni钢，以及异种金属的焊接。其耐裂性更为优越。

Be used to weld 29%Cr, 9%Ni steels, and different race metals,its crack-resistance more superior.

ER316

H08Cr19Ni12Mo2

Y316

ER316

2.0-4.5

0.08

0.3-0.65

1.0-2.5

0.03

0.03

18.0-20.0

11.0-14.0

2.0-3.0

0.75

用于18%Cr、12%Ni、2％Ｍo钢，其耐裂性、耐蚀性皆佳。

Be used to weld 18%Cr, 12%Ni, 2％Ｍo steels, its crack-resistance,corrosion-resistance more superior.

ER316L

H03Cr19Ni12Mo2

Y316L

ER316L

2.0-4.5

0.03

0.3-0.65

1.0-2.5

0.03

0.03

18.0-20.0

11.0-14.0

2.0-3.0

0.75

用于低碳18%Cr、12%Ni、2％Ｍo钢，耐蚀性更为优越。

Be used to weld low-carbon 18%Cr, 12%Ni, 2％Ｍo steels, its corrosion-reisitance more superior.

ER317L

H03Cr19Ni14Mo3

Y317L

ER317L

2.0-4.5

0.03

0.3-0.65

1.0-2.5

0.03

0.03

18.5-20.5

13.0-15.0

3.0-4.0

0.75

含较高的Ｍo及极低的碳，高温时仍具有高强度，对于硫酸、亚硫酸、有机酸等防蚀性有极佳的效果。

Contain the higher Mo and very the low carbon, heat hour still have the high strength, and defent the eclipse to have for sulfuric acid, sulfurous acid,organic acid¡ etc. very good result.

ER318

H08Cr19Ni12Mo2Nb

Y318

ER318

2.0-4.5

0.08

0.3-0.65

1.0-2.5

0.03

0.03

18.0-20.0

11.0-14.0

2.0-3.0

0.75

Nb:8×C-1.0

含Ｍo及Ｎb，耐热性、耐蚀性、粒间腐蚀皆优越。对于硫酸、亚硫酸、有机酸等防蚀性有极佳的效果。

Contain the Mo and Nb, heat-proof,bear the eclipse, grain to decay all superior. defend to eclipse contain good result for sulfuric acid, sulfurous acid, organic acid¡ etc.

ER347

H08Cr20Ni10Nb

Y347

ER347

2.0-4.5

0.08

0.3-0.65

1.0-2.5

0.03

0.03

19.0-21.5

9.0-11.0

0.75

0.75

Nb:10×C-1.0

含Ｎb，增加了粒间腐蚀的防蚀性，高温时强度大，适于耐热钢的焊接。

Contain the Nb, and increase the grain to decay of defend the eclipse, heat the hour strength big, used for the welding of heat-proof steel.

ER410

H12Cr13

Y410

ER410

2.0-4.5

0.12

0.5

0.6

0.03

0.03

11.5-13.5

0.6

0.75

0.75

用于13％Cr的马氏体不锈钢焊接，耐磨性及耐蚀性良好。

Be used to weld 13%Cr martensitic stainless steels, better whet-resistance and corrosion resistance.

ER430

H10Cr17

Y430

ER430

2.0-4.5

0.10

0.5

0.6

0.03

0.03

15.5-17.0

0.6

0.75

0.75

用于SUS430的焊接，耐磨性及耐蚀性良好。

Be used to weld SUS430 steels, better whet-resistance and corrosion resistance.